XL-100 are high-tensile macro mono-filament Polypropylene fibers for use in creating fiber-reinforced concrete (FRC). The primary benefits of XL-100 are shrinkage crack and thermal crack control as well as increased tensile and flexural strength enough to replace welded wire mesh.
Meets the requirements of ASTM C-1116, Section 4.1.3 and ASTM C-1399.
Bulk pricing available, contact us for a quote.
| Configuration | Monafilament |
|---|---|
| Tensile Strength | 100 ksi (690 MPa) |
| Flexural Strength | 1305 ksi (9.0 GPa) |
| Filament Diameter | .5 mm (500 microns) |
| Available Lengths | 1" (25 mm), 1.5" (38 mm) |
| Aspect-Ratio | 50,76 |
| Melting Point | 320o F (160o C) |
| Water Absorbtion | Nil |
| Color | White |
| Elongation | 25 |
| ZrO2 Content | NA |
XL-100 can be added directly to the mixing system during or after the batching of the ingredients and mixed at high speed for a minimum of five minutes. Additional mixing does not adversely affect the distribution or overall performance of XL-100. The addition of XL-100 at the normal recommended dosage rate (3-10 lb/cy) does not require any mix design or application changes. A water reducer or super-plasticizer is recommended in concrete products where improved workability and finishability are desired.
Industrial Slab on Grade, Composite Metal Deck, Precast, Welded Wire Mesh Replacement